Solution combustion synthesis of high-entropy metal spinel oxide as oxygen evolution reaction catalyst
文献摘要：
High-entropy metal spinel oxide (HEO) is proved to be a promising oxygen evolution reaction (OER) catalyst with high catalytic performance and stability. A short routine synthesis process based on solution combustion synthesis was proposed to prepare (Co0.25Ni0.25Mn0.25Zn0.25)Fe2O4 spinel HEO in this work. During the process, the products were rapidly synthesized and melted due to the high-temperature reaction, and then quickly crystallized on the surface of nickel foam to form a nano-structure coating. With the aid of nano-scale spinel structure, the overpotential of non-activation HEO electrode reaches 276 mV at the current density of 10 mA·cm-2, and after 100 h i-t test, it can be further reduced to 230 mV, which proves the high activity of OER catalysis. The promotion of OER catalytic performance can be attributed to the surface reconstruction caused by the selective element leaching and the boost of oxygen vacancy, leading to the formation of nano-scale flocculation around spinel core after the long-term OER process. This work indicates a special casting process for functional materials and explores the application of rapid crystallization.
文献关键词：
中图分类号：
作者姓名：
Tao Lu;Yue Zhang;Li Ding;Hao-yue Zheng;Ye Pan
作者机构：
文献出处：
引用格式：
[1]Tao Lu;Yue Zhang;Li Ding;Hao-yue Zheng;Ye Pan-.Solution combustion synthesis of high-entropy metal spinel oxide as oxygen evolution reaction catalyst)[J].中国铸造,2022(06):551-558
A类：
25Zn0
B类：
Solution,combustion,synthesis,high,entropy,metal,spinel,oxide,oxygen,evolution,reaction,catalyst,High,HEO,proved,be,promising,OER,catalytic,performance,stability,short,routine,process,solution,was,proposed,prepare,Co0,25Ni0,25Mn0,Fe2O4,this,work,During,products,were,rapidly,synthesized,melted,due,temperature,then,quickly,crystallized,surface,nickel,foam,nano,structure,coating,With,aid,scale,overpotential,activation,electrode,reaches,mV,current,density,mA,after,test,further,reduced,which,proves,activity,catalysis,promotion,attributed,reconstruction,caused,by,selective,element,leaching,boost,vacancy,leading,formation,flocculation,around,core,long,term,This,indicates,special,casting,functional,materials,explores,application,crystallization
AB值：
0.594309
相似文献
机标中图分类号，由域田数据科技根据网络公开资料自动分析生成，仅供学习研究参考。