Tailoring the Texture and Mechanical Properties of Textured-AZ31 Mg Alloy Sheets by Twinning and Recrystallization
文献摘要：
In this study,a method of corrugated width limit alignment processes(CWLA)was applied to pre-twin in hot-rolled Mg alloy sheets.The microstructure evolution and mechanical properties of the CWLA sheets were studied.The results demonstrated that the grain orientation was transformed from strong basal texture to RD-rotated texture after CWLA treatment and up to 22.2％of{10-12}tensile twin boundaries were produced in the microstructure.The 60±5°<10-10>twin variant pairs were dominant in the twinned microstructure.Two kinds of dynamic recrystallization(DRX)mechanism,i.e.,continu-ous DRX(CDRX)at low-temperature CWLA and the discontinuous DRX(DDRX)at high-temperature condition were observed.After post-annealing,the twin-induced static recrystallization(SRX)and abnormal grain growth were observed in the CWLA samples,and most twin boundaries were retained.After CAWL for 60 min at 300℃and post annealing,an improvement on plasticity and strength were achieved with 55％increment for uniform elongation(UE)and 10％increment for ultimate tensile strength(UTS).
文献关键词：
中图分类号：
作者姓名：
Hui-Hu Lu;You Li;Li Lu;Wang-Gang Zhang;Wei Liang
作者机构：
School of Mechanical Engineering,North University of China,Taiyuan 030051,China;College of Materials Science and Engineering,Taiyuan University of Technology,Taiyuan 030024,China
文献出处：
引用格式：
[1]Hui-Hu Lu;You Li;Li Lu;Wang-Gang Zhang;Wei Liang-.Tailoring the Texture and Mechanical Properties of Textured-AZ31 Mg Alloy Sheets by Twinning and Recrystallization)[J].金属学报（英文版）,2022(12):1983-1995
A类：
CWLA,CAWL
B类：
Tailoring,Mechanical,Properties,Textured,AZ31,Mg,Alloy,Sheets,by,Twinning,Recrystallization,In,this,study,method,corrugated,width,limit,alignment,processes,was,applied,pre,hot,rolled,alloy,sheets,microstructure,evolution,mechanical,properties,were,studied,results,demonstrated,that,grain,orientation,transformed,from,strong,basal,texture,RD,rotated,after,treatment,up,tensile,boundaries,produced,variant,pairs,dominant,twinned,Two,kinds,dynamic,recrystallization,mechanism,CDRX,low,temperature,discontinuous,DDRX,high,condition,observed,After,post,annealing,induced,static,SRX,abnormal,growth,samples,most,retained,improvement,plasticity,strength,achieved,increment,uniform,elongation,UE,ultimate,UTS
AB值：
0.57524
相似文献
机标中图分类号，由域田数据科技根据网络公开资料自动分析生成，仅供学习研究参考。