Selective Laser Melting of Carbon-Free Mar-M509 Co-Based Superalloy:Microstructure,Micro-Cracks,and Mechanical Anisotropy
文献摘要：
In this work,the microstructural evolution,micro-crack formation,and mechanical anisotropy of the selective laser melted(SLM)carbon-free Mar-M509 Co-based superalloy were systematically studied under different linear energy densities(LED).Observation shows that the SLM Mar-M509 superalloy possesses a fully dense structure,whereas some micro-cracks exist along the building direction.The electron backscatter diffraction results reveal that dominant columnar grains tend to elongate along the building direction parallel to the XZ plane.Meanwhile,both a<001>near fiber texture and a{100}<001>near sheet texture are observed in different specimens.For the specimen with fiber texture,a high misorienta-tion angle exists among different columnar grains,which aggravated the generation of micro-cracks under thermal stress.Higher LED results in higher micro-crack density in the SLM specimen due to higher thermal stress.Mar-M509 specimen fabricated under lower LED exhibits higher tensile strength due to more significant grain refinement.More prominent anisotropy of tensile performance was found in the high LED specimen,which can be attributed to the higher density of micro-cracks and crystallographic texture.Furthermore,the SLM Mar-M509 superalloy exhibits better mechanical proper-ties than the traditional cast technique.In summary,this work can contribute to the development and the future application of SLM-fabricated Co-based superalloy.
文献关键词：
中图分类号：
作者姓名：
Xiaodong Wang;Chaoyue Chen;Ruixin Zhao;Longtao Liu;Sansan Shuai;Tao Hu;Jiang Wang;Zhongming Ren
作者机构：
State Key Laboratory of Advanced Special Steels,School of Materials Science and Engineering,Shanghai University,Shanghai 200444,China
文献出处：
引用格式：
[1]Xiaodong Wang;Chaoyue Chen;Ruixin Zhao;Longtao Liu;Sansan Shuai;Tao Hu;Jiang Wang;Zhongming Ren-.Selective Laser Melting of Carbon-Free Mar-M509 Co-Based Superalloy:Microstructure,Micro-Cracks,and Mechanical Anisotropy)[J].金属学报（英文版）,2022(03):501-516
A类：
M509,misorienta
B类：
Selective,Laser,Melting,Carbon,Free,Mar,Co,Based,Superalloy,Microstructure,Cracks,Mechanical,Anisotropy,In,this,work,microstructural,evolution,formation,mechanical,anisotropy,selective,laser,melted,SLM,carbon,free,superalloy,were,systematically,studied,under,different,linear,energy,densities,LED,Observation,shows,that,possesses,fully,dense,whereas,some,cracks,along,building,direction,electron,backscatter,diffraction,results,reveal,dominant,columnar,grains,tend,elongate,parallel,XZ,plane,Meanwhile,both,fiber,texture,sheet,are,observed,specimens,For,angle,exists,among,which,aggravated,generation,thermal,stress,Higher,higher,density,due,fabricated,lower,exhibits,tensile,strength,significant,refinement,More,prominent,performance,was,found,attributed,crystallographic,Furthermore,better,proper,than,traditional,cast,technique,summary,contribute,development,future,application
AB值：
0.517627
相似文献
机标中图分类号，由域田数据科技根据网络公开资料自动分析生成，仅供学习研究参考。