Sub-micron Co-Al2O3 composite powders prepared by room-temperature ultrasonic-assisted electroless plating
文献摘要：
Sub-micron Co-Al2O3 composite powders were synthesized by ultrasonic-assisted electroless plating process at room temperature with a one-step activating method pretreatment.The effect of process parameters on plating rate,Co content,and the uniformity of cobalt layer was analyzed by transmission electron microscopy(TEM).The results show that as the initial pH values of plating bath increase,the plating rate increases.The plating rate declines as the load increases when the load of powders is less than 12 g·L-1,but increases when the load is greater than 12 g·L-1.The relative Co content of the Co-Al2O3 powder declines with the powder load increasing.
文献关键词：
中图分类号：
作者姓名：
Liu Zhu;Hong-Bo Guo;Sheng-Kai Gong
作者机构：
School of Materials Science and Engineering,Beihang University,Beijing 100191,China;Department of Mechanical Engineering,Taizhou University,Taizhou 318000,China
文献出处：
引用格式：
[1]Liu Zhu;Hong-Bo Guo;Sheng-Kai Gong-.Sub-micron Co-Al2O3 composite powders prepared by room-temperature ultrasonic-assisted electroless plating)[J].稀有金属（英文版）,2022(06):1968-1971
A类：
B类：
Sub,micron,Co,Al2O3,composite,powders,prepared,by,room,temperature,ultrasonic,assisted,electroless,plating,were,synthesized,process,one,step,activating,method,pretreatment,effect,parameters,rate,content,uniformity,cobalt,layer,was,analyzed,transmission,electron,microscopy,TEM,results,show,that,initial,values,bath,increases,declines,load,when,than,but,greater,relative,increasing
AB值：
0.478445
相似文献
机标中图分类号，由域田数据科技根据网络公开资料自动分析生成，仅供学习研究参考。