Wetting and corrosion behavior between magnesia-carbon refractory and converter slags with different MgO contents
文献摘要：
The influence of MgO content in slag on wetting and corrosion behavior between slag and MgO-C refractory was investigated.It can be known from the high-temperature wetting experiment that as the MgO content in the slag increases,the final contact angle between the slag and the MgO-C refractory gradually increases and the penetration depth of the slag into the refractory gradually decreases from 60.54 μm(when the MgO content is 8％)to 28.11 μm(when the MgO content is 12％).The CaO and SiO2 in the slag penetrate into the MgO-C refractory along the pores or surface cracks formed by carbon oxidation and react with MgO to generate a large amount of low-melting compound CaO-MgO-SiO2,which accelerates the corrosion of the refractory.As the MgO content in slag increases,the viscosity of the slag increases and the fluidity becomes worse,so that the mass transfer and diffusion of molecules or ions in the slag are weakened.In addition,the increase in MgO reduces the activity of FeO in the slag,which inhibits the interfacial chemical reaction,thereby weakening the wetting effect caused by the reaction.
文献关键词：
中图分类号：
作者姓名：
Rui-qiang Bai;Si-yang Liu;Fei-xiong Mao;Yuan-yuan Zhang;Xin Yang;Zhi-jun He
作者机构：
School of Materials and Metallurgy,University of Science and Technology Liaoning,Anshan 114051,Liaoning,China;Ningbo Key Laboratory of Marine Protection Materials,Ningbo Institute of Materials Technology and Engineering,Chinese Academy of Sciences,Ningbo 315201,Zhejiang,China
文献出处：
引用格式：
[1]Rui-qiang Bai;Si-yang Liu;Fei-xiong Mao;Yuan-yuan Zhang;Xin Yang;Zhi-jun He-.Wetting and corrosion behavior between magnesia-carbon refractory and converter slags with different MgO contents)[J].钢铁研究学报（英文版）,2022(07):1073-1079
A类：
B类：
Wetting,corrosion,behavior,between,magnesia,carbon,refractory,converter,slags,different,MgO,contents,influence,wetting,was,investigated,It,can,known,from,high,temperature,experiment,that,increases,final,contact,angle,gradually,penetration,depth,into,decreases,when,CaO,SiO2,penetrate,along,pores,surface,cracks,formed,oxidation,generate,large,amount,low,melting,compound,which,accelerates,viscosity,fluidity,becomes,worse,so,mass,transfer,diffusion,molecules,ions,are,weakened,In,addition,reduces,activity,FeO,inhibits,interfacial,chemical,reaction,thereby,weakening,effect,caused
AB值：
0.460641
相似文献
机标中图分类号，由域田数据科技根据网络公开资料自动分析生成，仅供学习研究参考。