Effect of Nb addition on microstructure and mechanical properties of 25CrNiMoV(DZ2)steel for high-speed railway axles
文献摘要：
The microstructure,precipitates and properties of 25CrNiMoV(DZ2)steel for high-speed railway axles with different Nb contents were investigated by means of optical microscopy,scanning electron microscopy,electron back-scattering diffraction,transmission electron microscopy and physicochemical phase analysis.The results show that the grain size of the original austenite of the test steels decreases from 20.5 to 14.2 and 10.8 μm after adding 0.026 and 0.039 wt.％Nb to a 25CrNiMoV steel,respectively.Moreover,the block width of the tempered martensite in the test steels is refined from 1.91 to 1.72 and 1.60 μm,respectively.MC-type precipitates in 25CrNiMoV steel are mainly VC,while(Nb,V)C gradually precipitates when Nb is microalloyed,and the amount of precipitates increases with increasing Nb content.Through strengthening mechanism analysis,it is found that grain refinement strengthening is the primary way to increase the strength.The improvement in the yield strength with increasing Nb content is attributed to a significant increase in precipitation strengthening,grain refinement strengthening and dislocation strengthening.
文献关键词：
中图分类号：
作者姓名：
Jin-wen Zhang;Yan-guang Cao;Cheng-guo Zhang;Zhao-dong Li;Wen-xian Wang
作者机构：
College of Materials Science and Engineering,Taiyuan University of Technology,Taiyuan 030024,Shanxi,China;Technology Center,Taiyuan Iron and Steel(Group)Co.,Taiyuan 030003,Shanxi,China;Department of Structural Steels,Central Iron and Steel Research Institute,Beijing 100081,China;Locomotive and Car Research Institute,China Academy of Railway Sciences Corporation Limited,Beijing 100081,China
文献出处：
引用格式：
[1]Jin-wen Zhang;Yan-guang Cao;Cheng-guo Zhang;Zhao-dong Li;Wen-xian Wang-.Effect of Nb addition on microstructure and mechanical properties of 25CrNiMoV(DZ2)steel for high-speed railway axles)[J].钢铁研究学报（英文版）,2022(05):802-809
A类：
25CrNiMoV,axles,microalloyed
B类：
Effect,Nb,addition,microstructure,mechanical,properties,DZ2,high,speed,railway,precipitates,different,contents,were,investigated,by,means,optical,microscopy,scanning,electron,back,scattering,diffraction,transmission,physicochemical,phase,analysis,results,show,that,grain,size,original,austenite,test,steels,decreases,from,after,adding,wt,respectively,Moreover,block,width,tempered,martensite,refined,MC,type,are,mainly,VC,while,gradually,when,amount,increases,increasing,Through,strengthening,mechanism,found,refinement,primary,improvement,yield,attributed,significant,precipitation,dislocation
AB值：
0.45473
相似文献
机标中图分类号，由域田数据科技根据网络公开资料自动分析生成，仅供学习研究参考。