Precipitation behavior of P550 steel for non-magnetic drill collars during isothermal aging at 650-900℃
文献摘要：
Precipitation behavior of P550 steel for non-magnetic drill collars was investigated by microstructure characterization as well as thermodynamic calculation.The results demonstrate that the main precipitate formed at 650-900℃was cellular Cr2N,and its precipitation depended heavily on the aging temperature.The most sensitive precipitation temperature of cellular Cr2N was 750℃.At 750℃,the cellular Cr2N exhibited fast-slow precipitation kinetics with the aging time prolonging.The initial precipitation of cellular Cr2N was governed by the short-range intergranular diffusion of Cr.During long-term aging,its growth was controlled by the long-range bulk diffusion of Cr.In addition,cellular Cr2N induced the precipitation of σ phase ahead of the cell after long period of aging.Increasing the nitrogen content resulted in the increment of both the nucleation site and the driving force for the cellular Cr2N,which jointly promoted its precipitation.
文献关键词：
中图分类号：
作者姓名：
Li-wei Xu;Huai-bei Zheng;Hua-bing Li;Zhou-hua Jiang;Shu-cai Zhang;Jiang-tao Yu;Hao Feng;Yue Lin
作者机构：
School of Metallurgy,Northeastern University,Shenyang 110819,Liaoning,China;State Key Laboratory of Metal Material for Marine Equipment and Application,Anshan 114002,Liaoning,China
文献出处：
引用格式：
[1]Li-wei Xu;Huai-bei Zheng;Hua-bing Li;Zhou-hua Jiang;Shu-cai Zhang;Jiang-tao Yu;Hao Feng;Yue Lin-.Precipitation behavior of P550 steel for non-magnetic drill collars during isothermal aging at 650-900℃)[J].钢铁研究学报（英文版）,2022(04):636-646
A类：
P550
B类：
Precipitation,behavior,steel,magnetic,drill,collars,during,isothermal,aging,was,investigated,by,microstructure,characterization,well,thermodynamic,calculation,results,demonstrate,that,main,precipitate,formed,cellular,Cr2N,its,precipitation,depended,heavily,temperature,most,sensitive,At,exhibited,fast,slow,kinetics,prolonging,initial,governed,short,range,intergranular,diffusion,During,term,growth,controlled,bulk,addition,induced,phase,ahead,after,period,Increasing,nitrogen,content,resulted,increment,both,nucleation,site,driving,force,which,jointly,promoted
AB值：
0.509625
相似文献
机标中图分类号，由域田数据科技根据网络公开资料自动分析生成，仅供学习研究参考。