Effect of copper on edge cracking behavior and microstructure of rolled austenitic stainless steel plate
文献摘要：
Cu is known to affect the edge cracking characteristics of austenitic stainless steel as it causes embrittlement.The hot rolling test of four kinds of austenitic stainless steel with different copper content(0,2.42,3.60 and 4.35 wt.％)was carried out to examine the effect of hot rolling cracks on steel containing different copper contents.The evolution of crack and microstructure was analyzed using the scanning electron microscope,energy-dispersive spectrometer,electron back scattered diffraction and transmission electron microscope.Experimental results showed an upward trend in edge cracking degree when Cu content was 4.35％,and the crack extended from the edge of the steel plate to the middle by about 14 mm.Besides,severe oxidation was observed inside the crack by fractography.With the increase in copper content at 1250℃,the content of{110}<112>brass and{112}<111>copper textures decreased.When the content of copper was 4.35％,the decrease was most significant,and{112}<111>copper texture content decreased to only 0.5％.Generally,the textures of 2.42％Cu and 3.60％Cu 304L steel changed little,while a large change in the texture of 4.35％Cu 304L steel was observed.To conclude,the increase in rolling temperature can prevent edge crack and its propagation effectively.
文献关键词：
中图分类号：
作者姓名：
Guang-hui Zhao;Jian Zhang;Juan Li;Hua-ying Li;Hai-tao Liu;Li-feng Ma
作者机构：
School of Mechanical Engineering,Taiyuan University of Science and Technology,Taiyuan 030024,Shanxi,China;Shanxi Provincial Key Laboratory of Metallurgical Device Design Theory and Technology,Taiyuan 030024,Shanxi,China;State Key Laboratory of Rolling and Automation,Northeastern University,Shenyang 110819,Liaoning,China
文献出处：
引用格式：
[1]Guang-hui Zhao;Jian Zhang;Juan Li;Hua-ying Li;Hai-tao Liu;Li-feng Ma-.Effect of copper on edge cracking behavior and microstructure of rolled austenitic stainless steel plate)[J].钢铁研究学报（英文版）,2022(02):281-294
A类：
B类：
Effect,copper,edge,cracking,behavior,microstructure,rolled,austenitic,stainless,steel,plate,known,affect,characteristics,causes,embrittlement,hot,rolling,test,four,kinds,different,wt,was,carried,examine,cracks,containing,contents,evolution,analyzed,using,scanning,electron,microscope,energy,dispersive,spectrometer,back,scattered,diffraction,transmission,Experimental,results,showed,upward,trend,degree,when,extended,from,middle,by,about,Besides,severe,oxidation,observed,inside,fractography,With,increase,brass,textures,decreased,When,most,significant,only,Generally,304L,changed,little,while,large,To,conclude,temperature,prevent,its,propagation,effectively
AB值：
0.476988
相似文献
机标中图分类号，由域田数据科技根据网络公开资料自动分析生成，仅供学习研究参考。