Metadynamic recrystallization and microstructure evolution of a continuously cast Ti-microalloyed steel slab with heavy reduction
文献摘要：
The effects of the deformation parameters in the heavy reduction(HR)process on recrystallization kinetics and microstructure evolution were analyzed.Based on the experimental results,metadynamic recrystallization(MDRX)kinetic and austenite grain size models were established for a continuously cast slab during HR.Moreover,the evolution of the quenched microstructure after MDRX was observed using electron backscatter diffraction.The relative frequency of very low-angle grain boundaries decreased from 58.8％to 52.1％,and the relative frequency of high-angle grain boundaries increased from 28.5％to 38.9％.Analyses revealed that the recovery was the main softening mechanism.The decrease in the total grain boundary length indicated that subgrain growth occurred with increasing inter-pass time.The main texture evolved from a{001}<110>texture to a{112}<111>texture,and the texture strength remained unchanged.
文献关键词：
中图分类号：
作者姓名：
Zi-jian Wei;Cheng Ji;Tian-ci Chen;Miao-yong Zhu;Chen-hui Wu
作者机构：
Key Laboratory for Ecological Metallurgy of Multimetallic Ores(Ministry of Education),Shenyang 110819,Liaoning,China;School of Metallurgy,Northeastern University,Shenyang 110819,Liaoning,China;Pangang Group Research Institute Co.,Ltd.,Panzhihua 617000,Sichuan,China
文献出处：
引用格式：
[1]Zi-jian Wei;Cheng Ji;Tian-ci Chen;Miao-yong Zhu;Chen-hui Wu-.Metadynamic recrystallization and microstructure evolution of a continuously cast Ti-microalloyed steel slab with heavy reduction)[J].钢铁研究学报（英文版）,2022(01):103-114
A类：
Metadynamic,microalloyed,metadynamic
B类：
recrystallization,microstructure,evolution,continuously,cast,Ti,steel,slab,heavy,reduction,effects,deformation,parameters,process,kinetics,were,analyzed,Based,experimental,results,MDRX,austenite,size,models,established,during,Moreover,quenched,after,was,observed,using,electron,backscatter,diffraction,relative,frequency,low,angle,boundaries,decreased,from,high,increased,Analyses,revealed,that,recovery,softening,mechanism,total,boundary,length,indicated,subgrain,growth,occurred,increasing,inter,pass,texture,evolved,strength,remained,unchanged
AB值：
0.528003
相似文献
机标中图分类号，由域田数据科技根据网络公开资料自动分析生成，仅供学习研究参考。