Significantly enhanced varistor properties via tailoring interface states were obtained in Ca1-2x/3YxCu3Ti4O12-SrCu3Ti4O12 composite ceramics.The breakdown field was improved to 35.8 kV cm-1 and the nonlinear coefficient in 0.1-1 mA cm-2 was enhanced to 14.6 for Ca0.67Y0.5Cu3Ti4O12-SrCu3Ti4O12.Noticeably,the withstand voltage of single grain boundary reached up to 24 V while the reported ones were constant to about 3 V.Greatly improved properties were attributed to the formation of superior grain boundary rather than the reduced grain size.Surprisingly,with distinct discrepancy of nonlinear performance in the composites,the resistance and activation energy of grain boundary exhibited little differences.Based on the double Schottky barrier at grain boundary and the field-assisted thermal emission model,it was found that the excellent electrical nonlinearity arose from the formation of deper and broader interface states at grain boundary.In this case,interface states were not easily entirely filled and the barrier could maintain its height under applied voltage.This work provides a novel routine for enhancing the varistor properties of CaCu3Ti4O12 based ceramics by manipulating interface states at grain boundary.

Zhuang Tang;Kai Ning;Zhiyao Fu;Ze Lian;Kangning Wu;Shoudao Huang

State Key Laboratory of Disaster Prevention and Reduction for Power Grid Transmission and Distribution Equipment,SGCC(State Grid Corporation of China),Changsha 410000,China;College of Electrical and Information Engineering,Hunan University,Changsha 410082,China;State Grid Shanxi Electric Power Research Institute,Taiyuan 030001,China;State Key Laboratory of Electrical Insulation and Power Equipment,Xi'an Jiaotong University,Xi'an 710049,China

材料科学技术（英文版）

[1]Zhuang Tang;Kai Ning;Zhiyao Fu;Ze Lian;Kangning Wu;Shoudao Huang-.Significantly enhanced varistor properties of CaCu3Ti4O12 based ceramics by designing superior grain boundary:Deepening and broadening interface states)[J].材料科学技术（英文版）,2022(13):82-89

varistor,3YxCu3Ti4O12,SrCu3Ti4O12,67Y0,5Cu3Ti4O12,Greatly,deper

Significantly,enhanced,properties,CaCu3Ti4O12,ceramics,by,designing,superior,grain,boundary,Deepening,broadening,interface,states,via,tailoring,were,obtained,Ca1,2x,breakdown,field,was,improved,kV,coefficient,mA,Ca0,Noticeably,withstand,voltage,single,reached,while,reported,ones,constant,about,attributed,formation,rather,than,reduced,size,Surprisingly,distinct,discrepancy,performance,composites,resistance,activation,energy,exhibited,little,differences,Based,double,Schottky,barrier,assisted,thermal,emission,model,found,that,excellent,electrical,nonlinearity,arose,from,broader,In,this,case,not,easily,entirely,filled,could,maintain,its,height,under,applied,This,work,provides,novel,routine,enhancing,manipulating