Unveiling the twinning and dynamic recrystallization behavior and the resultant texture evolution in the extruded Mg-Bi binary alloys during hot compression
文献摘要：
The twinning behavior,dynamic recrystallization(DRX)mechanism and the resultant texture evolution of the extruded Mg-xBi(x=0.5 wt.％,2.0 wt.％)alloys were systematically investigated during hot compres-sion at the strain rate of 10 s-1 and temperature of 200℃.The results indicate that the types and inten-sities of the texture are greatly dependent on the twining behavior and DRX mechanism.At the initial stage,the evolution of texture is mainly domination by the formation and variation of{1012}extension twins,which is beneficial to the compression direction(CD)-tilted basal texture.With an increase in the strain,the texture evolution is more greatly regulated by the DRX mechanism.Besides,the pyramidal＜c+a＞slip and basal＜a＞slip are activated during the compression process,resulting in the Schmid factors(SF)of pyramidal slip remain at～0.4 and the average SFs for basal＜a＞slip increase from 0.2 to 0.34 as the strain increase.These findings provide a new insight into controlling the texture of wrought Mg-Bi-based alloys during hot deformation processing.
文献关键词：
中图分类号：
作者姓名：
Yu-qin Zhang;Wei-li Cheng;Hui Yu;Hong-xia Wang;Xiao-feng Niu;Li-fei Wang;Hang Li
作者机构：
School of Materials Science and Engineering,Taiyuan University of Technology,Taiyuan 030024,China;Key Laboratory of Interface Science and Engineering in Advanced Materials Ministry of Education,Taiyuan University of Technology,Taiyuan 030024,China;School of Materials Science and Engineering,Hebei University of Technology,Tianjin 300132,China
文献出处：
引用格式：
[1]Yu-qin Zhang;Wei-li Cheng;Hui Yu;Hong-xia Wang;Xiao-feng Niu;Li-fei Wang;Hang Li-.Unveiling the twinning and dynamic recrystallization behavior and the resultant texture evolution in the extruded Mg-Bi binary alloys during hot compression)[J].材料科学技术（英文版）,2022(10):274-285
A类：
twining
B类：
Unveiling,twinning,dynamic,recrystallization,behavior,resultant,texture,evolution,extruded,Mg,binary,alloys,during,hot,compression,DRX,mechanism,xBi,wt,were,systematically,investigated,strain,rate,temperature,results,indicate,that,types,inten,sities,are,greatly,dependent,At,initial,stage,mainly,domination,by,variation,extension,twins,which,beneficial,direction,CD,tilted,basal,With,increase,more,regulated,Besides,pyramidal,c+a,slip,activated,resulting,Schmid,factors,remain,average,SFs,from,These,findings,provide,new,insight,into,controlling,wrought,deformation,processing
AB值：
0.489346
相似文献
机标中图分类号，由域田数据科技根据网络公开资料自动分析生成，仅供学习研究参考。