Tribological and Physicochemical Analysis of Squid Pen High-density Polyethylene Biocomposite for Medical Application
文献摘要：
High-Density Polyethylene(HDPE)wear debris generated in the hip joint prothesis leads to its loosening.The aim of this study was to evaluate the potential of Squid Pen(SP)on the tribological and physicochemical properties of HDPE matrix.Biocomposites filled with 0,5,10,15 and 20 wt.％SP were elaborated by hot compression molding.Wear tests were carried out using a reciprocating pin-on-disc tribometer.Rockwell hardness,Fourier-Transform infra-red(FTIR)analysis,Scanning Electron Microscopy(SEM)of the biocomposite were analysed.FTIR analysis results of the biocomposites showed that an increase in the crystallinity rate was obtained with the addition of SP filler.Only 10 wt.％of SP has a significant effect on the hardness of the composite.The correlation between the friction coefficient and the wear resistance of the composite was investigated.The 5 wt.％SP-HDPE biocomposite has the lowest friction coefficient value with a decrease in the specific wear rate,compared to the unfilled HDPE.The SEM results showed that SP wear debris played an important role as a third roller body at the interface reducing the friction coefficient of the composite.It was concluded that the HDPE biocomposite could be successfully reinforced with 5 wt.％of SP.
文献关键词：
中图分类号：
作者姓名：
Besma Sidia;Walid Bensalah
作者机构：
Mechanical Engineering Laboratory,L9ES32,National Engineering School of Monastir,University of Monastir,Monastir,Tunisia
文献出处：
引用格式：
[1]Besma Sidia;Walid Bensalah-.Tribological and Physicochemical Analysis of Squid Pen High-density Polyethylene Biocomposite for Medical Application)[J].仿生工程学报（英文版）,2022(05):1481-1492
A类：
Biocomposite,prothesis,Biocomposites,biocomposite,biocomposites
B类：
Tribological,Physicochemical,Analysis,Squid,Pen,High,density,Polyethylene,Medical,Application,Density,HDPE,wear,debris,generated,hip,joint,leads,its,loosening,aim,this,study,was,evaluate,potential,SP,tribological,physicochemical,properties,matrix,wt,were,elaborated,by,hot,compression,molding,Wear,tests,carried,out,using,reciprocating,pin,disc,tribometer,Rockwell,hardness,Fourier,Transform,infra,FTIR,analysis,Scanning,Electron,Microscopy,analysed,results,showed,that,increase,crystallinity,obtained,addition,filler,Only,has,significant,effect,correlation,between,friction,coefficient,resistance,investigated,lowest,value,decrease,specific,compared,unfilled,played,important,role,third,roller,body,interface,reducing,It,concluded,could,successfully,reinforced
AB值：
0.539104
相似文献
机标中图分类号，由域田数据科技根据网络公开资料自动分析生成，仅供学习研究参考。