Experimental and numerical investigations on the tensile mechanical behavior of marbles containing dynamic damage
文献摘要：
To investigate the degradation mechanism of static tensile mechanical behaviors of marble containing dynamic damage,multiple impact loading tests were performed on the disc marble samples,and then static Brazilian tests were conducted for the damaged samples.Besides,coupling modeling technology of finite difference method (FDM)-discrete element method (DEM) was used to carry out the numerical investigation.The results show that after multiple impacts,more white patches appear on the surface,and some microcracks,macro-fractures as well as pulverized grains are found by optical microscopic.The static tensile strength decreases with the increase of the dynamic damage variable characterized by the ultrasonic wave velocity of sample.The interaction between grains in the damaged sample becomes intense in the subsequent static loading process,causing a relatively large strain.The volume of the fragments falling off around the loading points becomes larger as impact number increases.As the dynamic damage increases,the absorbed energy of sample during the static loading first decreases and then tends to he stable.Both the stress concentration and the breakage of the force chains are the root causes of the degradation of the static tensile strength.
文献关键词：
中图分类号：
作者姓名：
Tao Zhang;Liyuan Yu;Haijian Su;Qiang Zhang;Shaobo Chai
作者机构：
State Key Laboratory for Geomechanics and Deep Underground Engineering,China University of Mining and Technology,Xuzhou 221116,China;School of Civil Engineering,Chang'an University,Xi'an 710064,China
文献出处：
引用格式：
[1]Tao Zhang;Liyuan Yu;Haijian Su;Qiang Zhang;Shaobo Chai-.Experimental and numerical investigations on the tensile mechanical behavior of marbles containing dynamic damage)[J].矿业科学技术学报（英文版）,2022(01):89-102
A类：
marbles
B类：
Experimental,numerical,investigations,tensile,mechanical,containing,dynamic,To,investigate,degradation,mechanism,static,behaviors,multiple,loading,tests,were,performed,samples,then,Brazilian,conducted,damaged,Besides,coupling,modeling,technology,finite,difference,method,FDM,discrete,element,DEM,was,used,carry,out,results,show,that,after,impacts,more,white,patches,appear,surface,some,microcracks,macro,fractures,well,pulverized,grains,are,found,by,optical,microscopic,strength,decreases,variable,characterized,ultrasonic,wave,velocity,interaction,between,becomes,intense,subsequent,process,causing,relatively,strain,volume,fragments,falling,off,around,points,larger,number,increases,absorbed,energy,during,first,tends,stable,Both,stress,concentration,breakage,force,chains,root,causes
AB值：
0.558423
相似文献
机标中图分类号，由域田数据科技根据网络公开资料自动分析生成，仅供学习研究参考。