Development and Application of Carbon-free Al2O3-MgO Dense Bricks for Steel Ladles
文献摘要：
Carbon-free Al2O3-MgO dense bricks were produced by the pressing method,using tabular alumina,white fused alumina,alumina micro-powder as main raw materials,and inorganic powder as the binder.The comprehensive properties and performance in steel ladle side wall were made a comparison between Al2O3-MgO dense bricks and precast blocks.The results show that Al2O3-MgO dense bricks exhibit high dense structure and strength,as well as superior thermal shock resistance and better penetration and corrosion resistance to slag than precast blocks.While replacing precast blocks with dense bricks in 250t steel ladle side wall in some domestic steel mills,the thickness of the metamorphic layer from slag penetration and the corrosion rate decrease evidently.The damage of dense bricks during service is mainly caused by the corrosion from molten steel and slag,and the structure spalling of the metamorphic layer also plays an important role.
文献关键词：
中图分类号：
作者姓名：
LUO Ming;FANG Binxiang;WEI Guoping;LIU Guangping;SHEN Mingke;SONG Yanan
作者机构：
Zhejiang Zili High Temperature Technology Co.,Ltd.,Shaoxing 312300,China;Zhejiang Zili Advanced Materials Co.,Ltd.,Shaoxing 312300,China
文献出处：
引用格式：
[1]LUO Ming;FANG Binxiang;WEI Guoping;LIU Guangping;SHEN Mingke;SONG Yanan-.Development and Application of Carbon-free Al2O3-MgO Dense Bricks for Steel Ladles)[J].中国耐火材料（英文版）,2022(02):35-39
A类：
Ladles
B类：
Development,Application,Carbon,free,Al2O3,MgO,Dense,Bricks,Steel,dense,bricks,were,produced,by,pressing,method,using,tabular,alumina,white,fused,micro,powder,raw,materials,inorganic,binder,comprehensive,properties,performance,steel,ladle,side,wall,made,comparison,between,precast,blocks,results,show,that,exhibit,high,structure,strength,well,superior,thermal,shock,resistance,better,penetration,corrosion,slag,than,While,replacing,250t,some,domestic,mills,thickness,metamorphic,layer,from,rate,decrease,evidently,damage,during,service,mainly,caused,molten,spalling,also,plays,important,role
AB值：
0.547854
相似文献
机标中图分类号，由域田数据科技根据网络公开资料自动分析生成，仅供学习研究参考。