In Situ Investigation of Si-Poisoning Effect in Al-Cu-Si Alloys Inoculated by Al-5Ti-1B
文献摘要：
In situ synchrotron X-radiography was carried out on Al-13Cu and Al-13Cu-7Si alloys with and without addition of Al-5Ti-1B master alloy.The effects of Si content on grain growth and the solute-suppressed nucleation zone (SSNZ) were quantitatively studied.The average grain size can be refined to 164 μm of Al-13Cu alloy inoculated by Al-5Ti-1B.After addition of 7％ Si content,a large number of TiB2 sites in the melt lost the inoculating ability due to "Si poisoning." The radius of the dendrite tip curvature of Al-13Cu is more than two times as large as that of Al-13Cu-7Si.The sharper tip is able to disperse the solute more effectively and thus grains can grow more rapidly.This causes that the dendrite arm growth rate with addition of 7％ Si solute is about 2.6 times that of no Si addition.In addition,the solute enrichment in the SSNZ of Al-13Cu is faster,and the area change of SSNZ is slower than that of Al-13Cu-7Si.Thus more nucleation sites in the SSNZ cannot be activated with addition of Si.This study will shed light on the understanding of Si poisoning in casting Al-Cu-Si alloys.
文献关键词：
中图分类号：
作者姓名：
Yiwang Jia;Dongfu Song;Nan Zhou;Kaihong Zheng;Yanan Fu;Da Shu
作者机构：
Guangdong Provincial Key Laboratory of Metal Toughening Technology and Application,Institute of New Materials,Guangdong Academy of Sciences,Guangzhou 510650,China;Shanghai Synchrotron Radiation Facility,Shanghai Institute of Applied Physics,Chinese Academy of Sciences,Shanghai 201204,China;Shanghai Key Lab of Advanced High-Temperature Materials and Precision Forming,School of Materials Science and Engineering,Shanghai Jiao Tong University,Shanghai 200240,China
文献出处：
引用格式：
[1]Yiwang Jia;Dongfu Song;Nan Zhou;Kaihong Zheng;Yanan Fu;Da Shu-.In Situ Investigation of Si-Poisoning Effect in Al-Cu-Si Alloys Inoculated by Al-5Ti-1B)[J].金属学报（英文版）,2022(01):146-156
A类：
Inoculated,13Cu,SSNZ,inoculating
B类：
Situ,Investigation,Poisoning,Effect,Alloys,by,5Ti,1B,situ,synchrotron,radiography,was,carried,7Si,alloys,without,addition,master,effects,content,growth,solute,suppressed,nucleation,zone,were,quantitatively,studied,average,size,refined,inoculated,After,large,number,TiB2,sites,melt,lost,ability,due,poisoning,radius,dendrite,tip,curvature,more,than,two,times,that,sharper,able,disperse,effectively,thus,grains,rapidly,This,causes,arm,rate,about,enrichment,faster,area,change,slower,Thus,cannot,activated,study,will,shed,light,understanding,casting
AB值：
0.414321
相似文献
机标中图分类号，由域田数据科技根据网络公开资料自动分析生成，仅供学习研究参考。