Entropy versus enthalpy in hexagonal-close-packed high-entropy alloys
文献摘要:
The addition of hexagonal-close-packed(hcp)non-rare-earth elements Zr,Ti and Co,to the 10-compo-nent hcp rare-earth-based high-entropy alloys(HEAs)with a composition of ScYLaNdGdTbDyHoErLuX(X=Zr,Co and Ti)was investigated.The enthalpy of mixing between elements was found to have a significant effect on the formation of phases.The addition of Co combines with elements that had a strong chemical affinity to form intermetallic compounds by the effect of enthalpy.Ti was added with all elements with poor chemical affinity and exhibited rejection to form a phase alone.These were the two terminal manifestations of the role of enthalpy over entropy.Part of Zr was soluble in the matrix under the action of entropy,while the other part had a greater affinity for Sc than the other elements to form a precipitate under the action of enthalpy.This was the result of the local balance between the effect of enthalpy and entropy.The solid solution of the elements had different degrees of strengthening effect,among which Zr had the most excellent strengthening effect from 185 to 355 MPa,so the solid solution strengthening model and precipitation strengthening model were proposed to predict the strength of the alloy with the addition of Zr effectively.
文献关键词:
作者姓名:
Xin-Wei Yang;Xiao-Hui Shi;Hui-Jun Yang;Jun-Wei Qiao;Peter K.Liaw;Yu-Cheng Wu
作者机构:
College of Materials Science and Engineering,Taiyuan University of Technology,Taiyuan 030024,China;School of Materials Science and Engineering,University of Tennessee,Knoxville 37996,USA;School of Materials Science and Engineering,Hefei University of Technology,Hefei 230000,China
引用格式:
[1]Xin-Wei Yang;Xiao-Hui Shi;Hui-Jun Yang;Jun-Wei Qiao;Peter K.Liaw;Yu-Cheng Wu-.Entropy versus enthalpy in hexagonal-close-packed high-entropy alloys)[J].稀有金属(英文版),2022(08):2906-2920
A类:
ScYLaNdGdTbDyHoErLuX
B类:
Entropy,versus,enthalpy,hexagonal,close,packed,high,entropy,alloys,addition,hcp,rare,earth,elements,Zr,Ti,Co,nent,HEAs,composition,was,investigated,mixing,between,found,have,significant,formation,phases,combines,that,had,strong,chemical,affinity,intermetallic,compounds,by,added,poor,exhibited,rejection,alone,These,were,two,terminal,manifestations,role,over,Part,soluble,matrix,under,action,while,other,part,greater,than,precipitate,This,result,local,balance,solid,solution,different,degrees,strengthening,among,which,most,excellent,from,model,precipitation,proposed,predict,effectively
AB值:
0.448152
相似文献
Effect of solid-solution strengthening on deformation mechanisms and strain hardening in medium-entropy V1-xCrxCoNi alloys
Hyun Chung;Dae Woong Kim;Woo Jin Cho;Heung Nam Han;Yuji Ikeda;Shoji Ishibashi;Fritz K?rmann;Seok Su Sohn-Department of Materials Science and Engineering,Korea University,Seoul 02841,South Korea;Center for High Entropy Alloys,Pohang University of Science and Technology,Pohang 37673,South Korea;Department of Materials Science and Engineering and Research Institute of Advanced Materials,Seoul National University,Seoul 08826,South Korea;Institute for Materials Science,University of Stuttgart,Pfaffenwaldring 55,Stuttgart 70569,Germany;Computational Materials Design,Max-Planck-Institut für Eisenforschung GmbH,Max-Planck-Strabe 1,Düisseldorf 40237,Germany;Research Center for Computational Design of Advanced Functional Materials(CD-Fmat),National Institute of Advanced Industrial Science and Technology(AIST),Tsukuba,Ibaraki 305-8568,Japan;Department of Materials Science and Engineering,Delft University of Technology,Mekelweg,2,Delft 2628 CD,the Netherlands
In situ neutron diffraction unravels deformation mechanisms of a strong and ductile FeCrNi medium entropy alloy
L.Tang;F.Q.Jiang;J.S.Wróbel;B.Liu;S.Kabra;R.X.Duan;J.H.Luan;Z.B.Jiao;M.M.Attallah;D.Nguyen-Manh;B.Cai-School of Metallurgy and Materials,University of Birmingham,B15 2TT,United Kingdom;Institute of Metal Research,Chinese Academy of Sciences,Shenyang 110016,China;Faculty of Materials Science and Engineering,Warsaw University of Technology,ul.Wo?oska 141,Warsaw 02-507,Poland;State Key Laboratory for Powder Metallurgy,Central South University,Changsha 410083,China;Rutherford Appleton Laboratory,ISIS Facility,Didcot OX11 0QX,United Kingdom;Department of Materials Science and Engineering,City University of Hong Kong,Kowloon,Hong Kong,China;Department of Mechanical Engineering,The Hong Kong Polytechnic University,Hung Hom,Hong Kong,China;CCFE,United Kingdom Atomic Energy Authority,Abingdon,Oxfordshire OX14 3DB,United Kingdom
Theoretical predictions and experimental verification on the phase stability of enthalpy-stabilized HE TMREB2s
Ze Zhang;Shizhen Zhu;Fu-Zhi Dai;Huimin Xiang;Yanbo Liu;Ling Liu;Zhuang Ma;Shijiang Wu;Fei Liu;Kuang Sun;Yanchun Zhou-School of Materials Science and Engineering,Beijing Institute of Technology,Beijing 100081,China;Science and Technology on Advanced Functional Composite Laboratory,Aerospace Research Institute of Materials and Processing Technology,Beijing 100076,China;National Key Laboratory of Science and Technology on Materials Under Shock and Impact,Beijing 100081,China;Yangtze Delta Region Academy of Beijing Institute of Technology,Jiaxing 314019,China;Beijing Institute of Technology Chongqing Innovation Center,Chongqing 401120,China;Zibo Firststar New Material Incorporated Co.,Ltd.,Zibo 255000,China;Shanghai Chenhua Science and Technology Corporation Ltd.,Shanghai 201804,China
机标中图分类号,由域田数据科技根据网络公开资料自动分析生成,仅供学习研究参考。