Hot cracking behavior of large size GH4742 superalloy vacuum induction melting ingot
文献摘要：
The developing of large size superalloy vacuum induction melting(VIM)ingots is limited owing to hot cracking.The hot cracking behavior of the large size GH4742 superalloy VIM ingot was investigated via experiment and simulation.The microstructure was examined by optical microscopy,and element segregation was investigated by electron probe microanalysis.The solidification temperature range and yield strength at high temperature(YSHT)were calculated by JMatPro software.The results show that the variations of microstructure and element segregation in different locations are caused by different cooling rates.Moreover,the larger secondary dendrite arm spacing and serious element segregation of Nb accelerate hot cracking of the VIM ingot.In addition,the solidification temperature range is wider,and YSHT is lower in center than at edge of the ingot.Therefore,the hot cracking susceptibility is the highest in the center of the GH4742 superalloy VIM ingot.The critical criterion of element segregation for hot cracking is that the partition coefficient of Nb should be larger than 0.5.
文献关键词：
中图分类号：
作者姓名：
Liang Zhang;Lei Wang;Yang Liu;Xiu Song;Teng Yu;Ran Duan
作者机构：
Key Laboratory for Anisotropy and Texture of Materials,Ministry of Education,School of Materials Science and Engineering,Northeastern University,Shenyang 110819,Liaoning,China;High Temperature Materials Division,Fushun Special Steel Co.,Ltd.,Fushun 113001,Liaoning,China;Gaona Aero Material Co.,Ltd.,Beijing 100081,China
文献出处：
引用格式：
[1]Liang Zhang;Lei Wang;Yang Liu;Xiu Song;Teng Yu;Ran Duan-.Hot cracking behavior of large size GH4742 superalloy vacuum induction melting ingot)[J].钢铁研究学报（英文版）,2022(09):1505-1512
A类：
YSHT
B类：
Hot,cracking,behavior,size,GH4742,superalloy,vacuum,induction,melting,developing,VIM,ingots,limited,owing,hot,was,investigated,via,experiment,simulation,microstructure,examined,by,optical,microscopy,element,segregation,electron,probe,microanalysis,solidification,temperature,range,yield,strength,were,calculated,JMatPro,software,results,show,that,variations,different,locations,caused,cooling,rates,Moreover,larger,secondary,dendrite,arm,spacing,serious,Nb,accelerate,In,addition,wider,lower,center,than,edge,Therefore,susceptibility,highest,critical,criterion,partition,coefficient,should
AB值：
0.453322
相似文献
机标中图分类号，由域田数据科技根据网络公开资料自动分析生成，仅供学习研究参考。