Investigation of stress corrosion cracking behavior and mechanism analysis of a 1900 MPa-grade ultra-high-strength stainless steel
文献摘要:
The stress corrosion cracking(SCC)behavior of a 1900 MPa-grade ultra-high-strength stainless steel in 3.5 wt.% NaCl solution was investigated by X-ray diffractometer,scanning electron microscopy,electron back-scattered diffraction,X-ray photoelectron spectroscopy,and potentiodynamic polarization curves.The results showed that USS122G steel has good SCC resistance,and the critical stress intensity factor(Kiscc)of USS122G steel was about 68.906 MPa m12 and Kiscc/KIC = 0.76(Kic is plane strain fracture toughness).The existence of film-like austenite along the lath martensite boundary and the protective effect of thecc passivation film were the main factors for its high KIscc.Among them,the main components of the passivation film on the surface of USS122G steel were Cr2O3,Cr(OH)3,FeOOH,and Ni(OH)2.The fracture morphology of SCC zone was intergranular and transgranular.Through the slow and fast scanning rate polar-ization curve test results,it can be concluded that SCC mechanism of USS122G steel in 3.5 wt.% NaCl solution at the open-circuit potential was a mixed mechanism involving hydrogen embrittlement and anodic dissolution.
文献关键词:
作者姓名:
Shuai Tian;Zhen-bao Liu;Ren-li Fu;Xiao-hui Wang;Jian-xiong Liang
作者机构:
School of Materials Science and Technology,Nanjing University of Aeronautics and Astronautics,Nanjing 210016,Jiangsu,China;Institute for Special Steel Institute,Central Iron and Steel Research Institute,Beijing 100081,China
引用格式:
[1]Shuai Tian;Zhen-bao Liu;Ren-li Fu;Xiao-hui Wang;Jian-xiong Liang-.Investigation of stress corrosion cracking behavior and mechanism analysis of a 1900 MPa-grade ultra-high-strength stainless steel)[J].钢铁研究学报(英文版),2022(09):1474-1484
A类:
USS122G,Kiscc,thecc,KIscc
B类:
Investigation,stress,corrosion,cracking,behavior,mechanism,analysis,grade,ultra,high,strength,stainless,steel,SCC,wt,NaCl,was,investigated,by,ray,diffractometer,scanning,microscopy,back,scattered,diffraction,photoelectron,spectroscopy,potentiodynamic,polarization,curves,results,showed,that,has,good,resistance,critical,intensity,about,m12,KIC,Kic,plane,strain,fracture,toughness,existence,film,like,austenite,along,lath,martensite,boundary,protective,effect,passivation,were,main,factors,its,Among,them,components,surface,Cr2O3,FeOOH,morphology,zone,intergranular,transgranular,Through,slow,fast,rate,test,concluded,open,circuit,potential,mixed,involving,hydrogen,embrittlement,anodic,dissolution
AB值:
0.531289
相似文献
New insights into the mechanism of localised corrosion induced by TiN-containing inclusions in high strength low alloy steel
Chao Liu;Reynier I.Revilla;Xuan Li;Zaihao Jiang;Shufeng Yang;Zhongyu Cui;Dawei Zhang;Herman Terryn;Xiaogang Li-Institute of Advanced Materials and Technology,University of Science and Technology Beijing,Beijing 100083,China;National Materials Corrosion and Protection Data Center,University of Science and Technology Beijing,Beijing 100083,China;Department of Materials and Chemistry,Research Group Electrochemical and Surface Engineering,Vrije Universiteit Brussel,Brussels,Belgium;School of Metallurgical and Ecological Engineering,University of Science and Technology Beijing,Beijing 100083,China;Department of Material Science and Engineering,Ocean University of China,Qingdao 266100,China
Characterizations of the biomineralization film caused by marine Pseudomonas stutzeri and its mechanistic effects on X80 pipeline steel corrosion
Haixian Liu;Wen Chen;Yu Tan;Guozhe Meng;Hongfang Liu;YFrank Cheng;Hongwei Liu-School of Chemical Engineering and Technology,Sun Yat-sen University,Zhuhai 519082,China;Research Institute of Natural Gas Technology,Southwest Oil&Gasfield Company,China National Petroleum Corporation,Chengdu 610000,China;Key Laboratory for Large-Format Battery Materials and System,Ministry of Education,Hubei Key Laboratory of Materials Chemistry and Service Failure,School of Chemistry and Chemical Engineering,Huazhong University of Science and Technology,Wuhan 430074,China;Department of Mechanical and Manufacturing Engineering,University of Calgary,Calgary,Alberta T2N 1N4,Canada
机标中图分类号,由域田数据科技根据网络公开资料自动分析生成,仅供学习研究参考。