Mechanism of high temperature reduction on iron carbide preparation with low-grade siderite
文献摘要：
The carburization roasting followed by magnetic separation is a feasible method to utilize low-grade siderite ore.In order to enhance the carburization efficiency and separation efficiency,high temperature reduction was carried out,and its mechanism was demonstrated by measuring carburization index,phase change,and microstructure under a carbon-sulfur infrared analyzer,an X-ray diffractometer,and a metallurgical microscope.The results show that both the carburization efficiency of siderite pellet and the separation efficiency of iron carbide from gangue are very low.However,high temperature reduction is a useful way to enhance the carburization efficiency,as it can accelerate the reduction reaction rate and carburization reaction rate.Furthermore,high temperature reduction can improve the growth of iron carbide particle,promote the carburization efficiency,and strengthen the sodium modification reactions,thereby greatly accel-erating the separation efficiency of iron carbide and gangue.When the siderite pellets were reduced at 1050℃ for 90 min and carburized at 650℃ for 120 min,the carburization index of carburized pellets reached 36.06.After magnetic separation treatment,an electric furnace burden assaying 83.12 wt.％ Fe and 6.96 wt.％ C was prepared,and the corre-sponding iron recovery rate was 95.43％.The high temperature reduction is promisingly adopted to promote the utilization of low-grade siderite ores using carburization-magnetic separation technology.
文献关键词：
中图分类号：
作者姓名：
Dong Chen;Ya-nan Lv;Wei Zhao;Fei-bao Wu;Wei-ang Ying
作者机构：
School of Iron and Steel,Soochow University,Suzhou 215021,Jiangsu,China;Department of Mechanical and Electrical Engineering,Suzhou Institute of Industrial Technology,Suzhou 215104,Jiangsu,China
文献出处：
引用格式：
[1]Dong Chen;Ya-nan Lv;Wei Zhao;Fei-bao Wu;Wei-ang Ying-.Mechanism of high temperature reduction on iron carbide preparation with low-grade siderite)[J].钢铁研究学报（英文版）,2022(09):1357-1367
A类：
carburization,assaying
B类：
Mechanism,high,temperature,reduction,iron,carbide,preparation,grade,siderite,roasting,followed,magnetic,separation,feasible,method,utilize,In,order,enhance,efficiency,was,carried,out,its,mechanism,demonstrated,measuring,phase,change,microstructure,under,carbon,sulfur,infrared,analyzer,ray,diffractometer,metallurgical,microscope,results,show,that,both,from,gangue,However,useful,way,can,accelerate,Furthermore,improve,growth,particle,promote,strengthen,sodium,modification,reactions,thereby,greatly,erating,When,pellets,were,reduced,carburized,reached,After,treatment,electric,furnace,burden,prepared,corre,sponding,recovery,promisingly,adopted,utilization,ores,using,technology
AB值：
0.430373
相似文献
机标中图分类号，由域田数据科技根据网络公开资料自动分析生成，仅供学习研究参考。