Development of new ductile iron with super-high thermal conductivity and elongation
文献摘要:
The effects of Si content,graphite volume fraction and pearlite volume fraction on the thermal conductivity of ductile iron were studied based on theoretical model analysis.Calculated results showed that the thermal conductivity of ductile iron was more sensitive to Si content compared with the volume fractions of pearlite and graphite.The key method to design and develop high thermal conductivity ductile iron was to control the Si content.Within 0.9-2.2 wt.%Si content,experimental results showed that with the increase in Si content,the thermal conductivity of ductile iron decreased dramatically,and the yield strength and tensile strength of ductile iron almost linearly increased,but the elongation remained almost unchanged.The dependence of thermal conductivity of ductile iron on temperature changed from monotonic decreasing to increasing first and then decreasing.Finally,we broke the common composition range of ductile iron and designed a new high C(≥3.9 wt.%)and low Si(1.0-1.4 wt.%)ductile iron with super-high thermal conductivity and elongation.Its thermal conductivity exceeded 40 W/(m K)within 27-300℃,and maintained at 35-40 W/(m K)at 500℃.The elongation was over 25%,and the tensile strength was more than 300 MPa.
文献关键词:
作者姓名:
Guang-hua Wang;Yan-xiang Li
作者机构:
School of Materials Science and Engineering,Tsinghua University,Beijing 100084,China;Key Laboratory for Advanced Materials Processing Technology,Ministry of Education,Beijing 100084,China
引用格式:
[1]Guang-hua Wang;Yan-xiang Li-.Development of new ductile iron with super-high thermal conductivity and elongation)[J].钢铁研究学报(英文版),2022(03):462-473
A类:
B类:
Development,new,ductile,iron,super,high,thermal,conductivity,elongation,effects,Si,content,graphite,volume,pearlite,were,studied,theoretical,model,analysis,Calculated,results,showed,that,was,more,sensitive,compared,fractions,key,method,develop,control,Within,wt,experimental,decreased,dramatically,yield,strength,tensile,almost,linearly,increased,but,remained,unchanged,dependence,temperature,from,monotonic,decreasing,increasing,first,then,Finally,broke,common,composition,range,designed,low,Its,exceeded,within,maintained,over,than
AB值:
0.410699
相似文献
Direct reduction swelling behavior of pellets in hydrogen-based shaft furnaces under typical atmospheres
Zichuan Zhao;Jue Tang;Mansheng Chu;Xindong Wang;Aijun Zheng;Xiaoai Wang;Yang Li-School of Metallurgy,Northeastern University,Shenyang 110819,China;Institute for Frontier Technologies of Low-carbon Steelmaking,Northeastern University,Shenyang 110819,China;Liaoning Province Engineering Research Center for Technologies of Low-Carbon Steelmaking,Northeastern University,Shenyang 110819,China;State Key Laboratory of Rolling and Automation,Northeastern University,Shenyang 110819,China;College of Materials Science and Engineering,Chongqing University,Chongqing 400044,China;HBIS Group Co.,Ltd,Shijiazhuang 050000,China;Xuanhua Iron and Steel Group Co.,Ltd,Shijiazhuang 075100,China;Iron and Steel Research Institute of HBIS Group Co.,Ltd,Shijiazhuang 050000,China
In situ neutron diffraction unravels deformation mechanisms of a strong and ductile FeCrNi medium entropy alloy
L.Tang;F.Q.Jiang;J.S.Wróbel;B.Liu;S.Kabra;R.X.Duan;J.H.Luan;Z.B.Jiao;M.M.Attallah;D.Nguyen-Manh;B.Cai-School of Metallurgy and Materials,University of Birmingham,B15 2TT,United Kingdom;Institute of Metal Research,Chinese Academy of Sciences,Shenyang 110016,China;Faculty of Materials Science and Engineering,Warsaw University of Technology,ul.Wo?oska 141,Warsaw 02-507,Poland;State Key Laboratory for Powder Metallurgy,Central South University,Changsha 410083,China;Rutherford Appleton Laboratory,ISIS Facility,Didcot OX11 0QX,United Kingdom;Department of Materials Science and Engineering,City University of Hong Kong,Kowloon,Hong Kong,China;Department of Mechanical Engineering,The Hong Kong Polytechnic University,Hung Hom,Hong Kong,China;CCFE,United Kingdom Atomic Energy Authority,Abingdon,Oxfordshire OX14 3DB,United Kingdom
机标中图分类号,由域田数据科技根据网络公开资料自动分析生成,仅供学习研究参考。