Effect of Al2O3/Na2O ratio and MnO on high-temperature properties of mold flux for casting peritectic steel
文献摘要：
The influences of Al2O3/Na2O ratio and MnO content on high-temperature properties,such as melting,crystallization,heat transfer,and viscosity of mold flux for casting peritectic steel,have been investigated.The results show that the melting temperatures of mold flux decrease,whereas the ratio of crystalline layers increases with the decrease in Al2O3/Na2O ratio and increase in MnO content.The average response temperatures of the three mold fluxes decrease from 566,525,to 512℃,respectively,which indicates that the heat transfer controlling ability of mold flux is promoted due to the increase in crystallization ability and addition of transition metal oxide MnO.Furthermore,the viscosity-temperature curves suggest that the viscosity at 1300℃decreases,but the break temperature increases with the reduction in Al2O3/Na2O and addition of MnO.
文献关键词：
中图分类号：
作者姓名：
Le-jun Zhou;Hao Luo;Wan-lin Wang;Xiong Yan;Hou-fa Wu
作者机构：
School of Metallurgy and Environment,Central South University,Changsha 410083,Hunan,China;National Center for International Cooperation of Clean Metallurgy,Changsha 410083,Hunan,China
文献出处：
引用格式：
[1]Le-jun Zhou;Hao Luo;Wan-lin Wang;Xiong Yan;Hou-fa Wu-.Effect of Al2O3/Na2O ratio and MnO on high-temperature properties of mold flux for casting peritectic steel)[J].钢铁研究学报（英文版）,2022(01):53-60
A类：
B类：
Effect,Al2O3,Na2O,ratio,MnO,high,properties,mold,casting,peritectic,steel,influences,content,such,melting,crystallization,heat,transfer,viscosity,have,been,investigated,results,show,that,temperatures,whereas,crystalline,layers,increases,average,response,three,fluxes,from,respectively,which,indicates,controlling,ability,promoted,due,addition,transition,metal,oxide,Furthermore,curves,suggest,decreases,but,break,reduction
AB值：
0.424567
相似文献
机标中图分类号，由域田数据科技根据网络公开资料自动分析生成，仅供学习研究参考。