Rate-dependent mechanical behavior of single-,bi-,twinned-,and poly-crystals of CoCrFeNi high-entropy alloy
文献摘要：
While considerable effort is made to understand the solid solution strengthening on the deformation behavior of high-entropy alloys(HEAs),relatively little attention is paid to the role of microstructural interfaces,especially twin boundaries(TBs),on the strain-rate sensitivity(SRS)of them.To address this,we have conducted micropillar compression experiments on single-,bi-,and twinned-crystals of CoCr-FeNi HEA and compared the results with those obtained with uniaxial tensile and compression tests on polycrystalline bulk samples.Results show that SRS,as well as the yield strength and plastic flow behav-ior,in single crystals are orientation dependent due to the differences in the maximum Schmid factors.While the high-angle grain boundaries arrest dislocation motion,TBs allow for dislocation transmission through them,which result in distinct mechanical responses.While the bi-crystal's deformation behav-ior is controlled by the'hard'grain,twinned crystals exhibit an'averaged'response.The large diversity of the reported SRS values in face centered cubic HEAs could be due to the varying fractions and thus contributions of annealing twins in the tested samples.
文献关键词：
中图分类号：
作者姓名：
Siyuan Wei;Yakai Zhao;Jae-il Jang;Upadrasta Ramamurty
作者机构：
School of Mechanical and Aerospace Engineering,Nanyang Technological University,639798,Republic of Singapore;Division of Materials Science and Engineering,Hanyang University,Seoul 04763,Republic of Korea;Technology and Research,Institute of Materials Research and Engineering,Agency for Science,138634,Republic of Singapore
文献出处：
引用格式：
[1]Siyuan Wei;Yakai Zhao;Jae-il Jang;Upadrasta Ramamurty-.Rate-dependent mechanical behavior of single-,bi-,twinned-,and poly-crystals of CoCrFeNi high-entropy alloy)[J].材料科学技术（英文版）,2022(25):253-264
A类：
B类：
Rate,dependent,mechanical,behavior,single,twinned,crystals,CoCrFeNi,high,entropy,While,considerable,effort,made,understand,solid,solution,strengthening,deformation,alloys,HEAs,relatively,little,attention,paid,role,microstructural,interfaces,especially,boundaries,TBs,strain,rate,sensitivity,SRS,them,To,address,this,have,conducted,micropillar,compression,experiments,compared,results,those,obtained,uniaxial,tensile,tests,polycrystalline,bulk,samples,Results,show,that,well,yield,plastic,flow,orientation,due,differences,maximum,Schmid,factors,angle,grain,arrest,dislocation,motion,allow,transmission,through,which,distinct,responses,controlled,by,hard,exhibit,averaged,large,diversity,reported,values,centered,cubic,could,varying,fractions,thus,contributions,annealing,twins,tested
AB值：
0.554796
相似文献
机标中图分类号，由域田数据科技根据网络公开资料自动分析生成，仅供学习研究参考。