Y2O3 modification on nickel-rich LiNi0.8Co0.1Mn0.1O2 with improved electrochemical performance in lithium-ion batteries
文献摘要:
Doping and coating are frequently employed for the improvement of the properties of Ni-rich NCM materials.In this work,we prepared stable LiNi0.8Co0.1Mn0.1O2 (NCM811) materials modified with Y2O3 via a wet chemical method.In order to investigate the action mechanism of Y2O3 on NCM811,we analyzed the microstructures using X-ray diffraction (XRD),X-ray photoelectron spectroscopy (XPS),scanning electron microscopy (SEM),and transmission electron microscopy (TEM).Also,to study the electrochemical performances,we conducted a charge/discharge test and cyclic voltammetry.Our results show that Y2O3 modified NCM811 materials have good thermal stability,and proper content of Y2O3 can effectively prevent the materials from damaging and significantly improve the electrochemical proper-ties of the materials.Particularly,1% Y2O3 modified NCM811 material show much better cycling per-formance than other samples.During cycling at 1.0C,the 1% Y2O3 modified NCM811 shows capacity retention of 90.1% after 100 cycles,which is higher than 69.4% for pristine NMC811.We examined the microstructures of the materials before and after circulation.Using the SEM results,we conclude that structural changes are among the key factors that lead to the degradation of the electrochemical properties of materials.
文献关键词:
作者姓名:
Rui He;Xue Bai;Aijia Wei;Lihui Zhang;Peng Liu;Zhenfa Liu
作者机构:
Institute of Energy Resources,Hebei Academy of Science,Shijiazhuang 050081,China;Hebei Engineer Research Center for Water Saving in Industry,Shijiazhuang 050081,China;Shijiazhuang Suntec-Chem Co.,Ltd,Shijiazhuang 050000,China
引用格式:
[1]Rui He;Xue Bai;Aijia Wei;Lihui Zhang;Peng Liu;Zhenfa Liu-.Y2O3 modification on nickel-rich LiNi0.8Co0.1Mn0.1O2 with improved electrochemical performance in lithium-ion batteries)[J].稀土学报(英文版),2022(02):309-317
A类:
B类:
Y2O3,modification,nickel,rich,LiNi0,8Co0,1Mn0,1O2,improved,electrochemical,lithium,batteries,Doping,coating,frequently,employed,improvement,properties,materials,In,this,work,prepared,stable,NCM811,modified,via,wet,method,order,investigate,mechanism,analyzed,microstructures,using,ray,diffraction,photoelectron,spectroscopy,XPS,scanning,microscopy,transmission,TEM,Also,study,performances,conducted,discharge,test,cyclic,voltammetry,Our,results,that,have,good,thermal,stability,content,effectively,prevent,from,damaging,significantly,Particularly,much,better,cycling,than,other,samples,During,0C,shows,capacity,retention,after,cycles,which,higher,pristine,NMC811,We,examined,before,circulation,Using,conclude,structural,changes,among,key,factors,lead,degradation
AB值:
0.529837
相似文献
MXene-wrapped ZnCo2S4 core-shell nanospheres via electrostatic self-assembly as positive electrode materials for asymmetric supercapacitors
Ji-Qiu Qi;Chen-Chen Zhang;Hao Liu;Lei Zhu;Yan-Wei Sui;Xiu-Juan Feng;Wen-Qing Wei;Hao Zhang;Peng Cao-Jiangsu Province Engineering Laboratory of High Efficient Energy Storage Technology and Equipments,School of Materials Science and Physics,China University of Mining and Technology,Xuzhou 221116,China;The School of Mines,China University of Mining and Technology,Xuzhou 221116,China;School of Mechanical-Electronic and Vehicle Engineering,Weifang University,Weifang 261061,China;Ningbo Institute of Materials Technology&Engineering,Chinese Academy of Sciences,Ningbo 315201,China;Department of Chemical&Materials Engineering,University of Auckland,Auckland 1142,New Zealand
Self-ball milling strategy to construct high-entropy oxide coated LiNi0.8Co0.1Mn0.1O2 with enhanced electrochemical performance
Kai YUAN;Tianzhe TU;Chao SHEN;Lin ZHOU;Jixuan LIU;Jing LI;Keyu XIE;Guojun ZHANG-State Key Laboratory of Solidification Processing,Center for Nano Energy Materials,School of Materials Science and Engineering,Northwestern Polytechnical University,Xi'an 710072,China;State Key Laboratory for Modification of Chemical Fibers and Polymer Materials,Institute of Functional Materials,College of Materials Science and Engineering,Donghua University,Shanghai 201620,China;Research&Development Institute of Northwestern Polytechnical University in Shenzhen,Northwestern Polytechnical University,Shenzhen 518057,China;State Key Laboratory of Environment-friendly Energy Materials,School of Materials Science and Engineering,Southwest University of Science and Technology,Mianyang 621010,China
机标中图分类号,由域田数据科技根据网络公开资料自动分析生成,仅供学习研究参考。