Effect of Porous Copper Pore Density on Joint Interface:Microstructure and Mechanical Analysis
文献摘要：
The effect of the pore density of porous copper ( Cu) on brazed Cu/porous Cu was investigated. A filler with a composition of Cu-9. 0Sn-7. 0Ni-6. 0P ( Sn:Tin;Ni:Nickel;P:Phosphorus) and porous Cu with pore densities of 15 pores per inch ( PPI) , 25 PPI, and 50 PPI were employed. The joint strength of Cu/ porous Cu was evaluated with shear tests at different brazing temperatures. Characterizations of the joint interface and fractured surface were achieved with scanning electron microscope ( SEM) , energy dispersive X-ray spectroscopy ( EDX) , and X-ray diffraction ( XRD) . The micro-hardness test of Cu/porous Cu joint interface showed a high hardness value ( HV) for 50 PPI porous Cu. This result was in line with its low shear strength. It was proved that the joint strength of Cu/porous Cu is dependent on the pore density of the porous Cu structure and brittle phases of Cu3 P and Ni3 P in the brazed interface.
文献关键词：
中图分类号：
作者姓名：
Nur Amirah Mohd Zahri;Farazila Yusof;Yukio Miyashita;Tadashi Ariga;A.S.Md.Abdul Haseeb;Nazatul Liana Sukiman
作者机构：
Department of Mechanical Engineering,Faculty of Engineering,University of Malaya,Kuala Lumpur 50603,Malaysia;Department of Mechanical Engineering,Faculty of Engineering and Advanced Manufacturing&Material Processing(AMMP Centre),University of Malaya,Kuala Lumpur 50603,Malaysia;Department of Mechanical Engineering,Nagaoka University of Technology,Nagaoka 940-2188,Japan;Department of Metallurgical Engineering,TokaiUniversity,Hiratsuka 259-1292,Japan;Department of Mechanical Engineering,Faculty of Engineering andCentre of Advanced Materials(CAM),University of Malaya,Kuala Lumpur 50603,Malaysia
文献出处：
引用格式：
[1]Nur Amirah Mohd Zahri;Farazila Yusof;Yukio Miyashita;Tadashi Ariga;A.S.Md.Abdul Haseeb;Nazatul Liana Sukiman-.Effect of Porous Copper Pore Density on Joint Interface:Microstructure and Mechanical Analysis)[J].哈尔滨工业大学学报（英文版）,2022(01):24-31
A类：
B类：
Effect,Porous,Copper,Pore,Density,Joint,Interface,Microstructure,Mechanical,Analysis,effect,density,porous,copper,brazed,was,investigated,filler,composition,0Sn,0Ni,0P,Tin,Nickel,Phosphorus,densities,pores,inch,PPI,were,employed,joint,strength,evaluated,shear,tests,different,brazing,temperatures,Characterizations,interface,fractured,surface,achieved,scanning,electron,microscope,energy,dispersive,ray,spectroscopy,EDX,diffraction,hardness,showed,high,value,HV,This,result,line,its,low,It,proved,that,dependent,brittle,phases,Cu3,Ni3
AB值：
0.57131
相似文献
机标中图分类号，由域田数据科技根据网络公开资料自动分析生成，仅供学习研究参考。