Oxidation induced ductility enhancement of Zr based metallic glass ribbons in vicinity of glass transition temperature
文献摘要：
Zr-based metallic glasses (MGs) possess a wide supercooled liquid region, which gives a wide processing window for superplastic forming to make microdevices with demanding size accuracy and surface finishing. The existence of oxygen may have an influence on the thermoplastic deformation process. Therefore, the effect of oxidation on the mechanical behavior of the MGs in the vicinity of glass transition temperature is of great significance for practical forming of MG components. In the present study, the effect of oxidation on tensile properties of Zr50Cu40Al10 metallic glass was investigated. The tested samples were characterized by XRD and SEM analysis. For the samples tested in air, the strength decreases 187 MPa, 61 MPa and 59 MPa and the ductility increases 0.31, 0.36, and 0.77 at 420 ℃, 430 ℃, and 440 ℃, respectively, compared with those tested in flowing argon. ZrO2 preferentially formed during the tensile testing at 420 ℃, and both ZrO2 and Al2O3 oxides formed at 430 ℃. The dilution of Zr elements in the remaining amorphous matrix caused by preferential oxidation on the surface layer attributes to the decrease in strength and enhancement in ductility of the Zr50Cu40Al10 metallic glasses.
文献关键词：
中图分类号：
作者姓名：
Jin-tao Wang;Xue-feng Gao;Rui-chun Wang;Yin-xiao Wang;Fu-yu Dong;Wen-ying Xue;Hong-wang Yang
作者机构：
School of Materials Science and Engineering,Shenyang University of Technology,Shenyang 110870,China;School of Intelligent Manufacturing,Weifang University of Science&Technology,Shouguang 262700,Shandong,China;State Key Lab of Rolling&Automation,Northeastern University,Shenyang 110819,China
文献出处：
引用格式：
[1]Jin-tao Wang;Xue-feng Gao;Rui-chun Wang;Yin-xiao Wang;Fu-yu Dong;Wen-ying Xue;Hong-wang Yang-.Oxidation induced ductility enhancement of Zr based metallic glass ribbons in vicinity of glass transition temperature)[J].中国铸造,2022(01):75-80
A类：
Zr50Cu40Al10
B类：
Oxidation,induced,ductility,enhancement,metallic,ribbons,vicinity,transition,temperature,glasses,MGs,possess,wide,supercooled,liquid,region,which,gives,processing,window,superplastic,forming,make,microdevices,demanding,size,accuracy,surface,finishing,existence,oxygen,may,have,influence,thermoplastic,deformation,Therefore,effect,oxidation,mechanical,behavior,great,significance,practical,components,In,present,study,tensile,properties,was,investigated,tested,samples,were,characterized,by,analysis,For,air,strength,decreases,increases,respectively,compared,those,flowing,argon,ZrO2,preferentially,formed,during,testing,both,Al2O3,oxides,dilution,elements,remaining,amorphous,matrix,caused,layer,attributes
AB值：
0.539442
相似文献
机标中图分类号，由域田数据科技根据网络公开资料自动分析生成，仅供学习研究参考。