Thermoelectric characteristics of flexible reduced graphene oxide/silver selenide nanowire composites prepared by a facile vacuum filtration process
文献摘要：
The reduced graphene oxide/silver selenide nanowire (rGO/Ag2Se NW) composite powders were fabricated via a wet chemical approach,and then flexible rGO/Ag2Se NW composite film was prepared by a facile vacuum filtration method combined with cold-pressing treatment.A highest power factor of 228.88 μW·m-1·K-2 was obtained at 331 K for the cold-pressed rGO/Ag2Se NW composite film with 0.01 wt％ rGO.The rGO/Ag2Se NW composite film revealed superior flexibility as the power factor retained 94.62％ after bending for 500 times with a bending radius of 4 mm,which might be due to the interwoven network structures of Ag2Se NWs and pliability of rGO as well as nylon membrane.These results demonstrated that the GO/Ag2Se NW composite film has a potential for preparation of flexible thermoelectric devices.
文献关键词：
中图分类号：
作者姓名：
Zuo Xiao;Yong Du;Qiufeng Meng;Lei Wang
作者机构：
School of Materials Science and Engineering,Shanghai Institute of Technology,Shanghai 201418,China
文献出处：
引用格式：
[1]Zuo Xiao;Yong Du;Qiufeng Meng;Lei Wang-.Thermoelectric characteristics of flexible reduced graphene oxide/silver selenide nanowire composites prepared by a facile vacuum filtration process)[J].中国物理B（英文版）,2022(02):66-71
A类：
pliability
B类：
Thermoelectric,characteristics,flexible,reduced,graphene,oxide,silver,selenide,nanowire,composites,prepared,by,facile,vacuum,filtration,process,rGO,Ag2Se,powders,were,fabricated,via,wet,chemical,approach,then,film,was,method,combined,cold,pressing,treatment,highest,power,obtained,pressed,wt,revealed,superior,flexibility,retained,after,bending,times,radius,which,might,due,interwoven,network,structures,NWs,well,nylon,membrane,These,results,demonstrated,that,has,potential,preparation,thermoelectric,devices
AB值：
0.517056
相似文献
机标中图分类号，由域田数据科技根据网络公开资料自动分析生成，仅供学习研究参考。