Experimental and analytical assessment of the hypervelocity impact damage of GLAss fiber REinforced aluminum
文献摘要：
This article addresses the response of GLAss fiber REinforced aluminum to hypervelocity impacts of micrometeoroid analogs at impact velocities of 7 km/s and beyond.In relation,the damage modes of different GLAss fiber REinforced aluminum configurations have been exemplified.The GLAss fiber REinforced aluminum configurations comprised six to twelve variably thick aluminum layers and up to four plies of glass fiber reinforced epoxy per composite laminate.Hypervelocity impact experiments have been conducted with the help of a two-stage light-gas gun,wherein aluminum-and stainless steel projectiles were launched at velocities up to 7.15 km/s.Visual inspection of the damage area suggested the dissipation of impact energy in elastic-plastic deformation,petalling,delamination,debonding,tensile failure of fibers,and pyrolysis of epoxy.A prevailing damage mode was not apparent albeit.The quasi-isotropic ply orientation of S2-glass/FM94-epoxy laminates promoted the interference of shock-and rarefaction waves and suppressed the damage area of GLAss fiber REinforced aluminum.To discriminate between the impact performance of different GLAss fiber REinforced aluminum configu-rations,the energy dissipated in different damage modes of GLAss fiber REinforced aluminum has been assessed quantitatively.In terms of normalized energy,the cross-ply GLAss fiber REinforced aluminum dissipated higher energy in petal formation than in other primary damage modes.The normalized petalling energy was found to decline with the increase of impact energy.The outcomes of this study will help to optimize the GLAss fiber REinforced aluminum laminate,which will be employed as a bumper shield to prevent the fatal damage and the unzipping of a spacecraft pressure bulkhead.
文献关键词：
中图分类号：
作者姓名：
Md.Zahid Hasan
作者机构：
Bangladesh Air Force Academy,Bangladesh Air Force Base Matiur Rahman,BAF Academy Road,7404 Jessore,Khulna,Bangladesh
文献出处：
引用格式：
[1]Md.Zahid Hasan-.Experimental and analytical assessment of the hypervelocity impact damage of GLAss fiber REinforced aluminum)[J].防务技术,2022(07):1232-1246
A类：
GLAss,REinforced,micrometeoroid,Hypervelocity,petalling,FM94,bumper,unzipping
B类：
Experimental,analytical,assessment,hypervelocity,damage,aluminum,This,article,addresses,response,impacts,analogs,velocities,beyond,In,relation,modes,different,configurations,have,been,exemplified,comprised,six,twelve,variably,thick,layers,four,plies,glass,reinforced,epoxy,composite,experiments,conducted,help,two,stage,light,gas,gun,wherein,stainless,steel,projectiles,were,launched,Visual,inspection,area,suggested,dissipation,energy,elastic,plastic,deformation,delamination,debonding,tensile,failure,fibers,pyrolysis,prevailing,was,not,apparent,albeit,quasi,isotropic,ply,orientation,S2,laminates,promoted,interference,shock,rarefaction,waves,suppressed,To,discriminate,between,performance,dissipated,has,assessed,quantitatively,terms,normalized,cross,higher,than,other,primary,found,decline,increase,outcomes,this,study,will,optimize,which,employed,shield,prevent,fatal,spacecraft,pressure,bulkhead
AB值：
0.441979
相似文献
机标中图分类号，由域田数据科技根据网络公开资料自动分析生成，仅供学习研究参考。